TECHNICAL INFO |
NOTE |
STONE SLAB SIZE · Standard Size: 3030*1430mm (119"x56") · Jumbo Size: 3230*1630mm (127"x64") · Super Jumbo Size: 3530*2030mm (139"x79") STONE THICKNESS · 8mm · 12mm · 15mm · 20mm · 30mm AVAILABLE SURFACE · Polished Surface · Matt Surface (Honed) · Leather Surface |
Bestone Quartz Surface is produced with up-to-date technology and fresh mined natural quartz stone grains, which makes the product resistant to external forces. During production process, resin and couplings are necessarily added to provide a certain flexibility to the product and minimize the fragile attribute. Hence a thermal shock might cause damage to the resin and the stone surface. What's more, when the quartz surfaces are exposed to direct sunlight for a long time, the whole slab might be warped and the color will be faded away because of the UV light. Therefore, a certain handling guidance must be applied when it comes to unload, store, fabricate and install the quartz stone surfaces. For more information or HD photos & videos, please contact our sales team: Email: [email protected] |
INGREDIENTS OF BESTONE'S ARTIFICIAL QUARTZ STONE |
INGREDIENT | PROPORTION | RAW MATERIAL | INGREDIENT | PROPORTION | INGREDIENT | PROPORTION |
QUARTZ SAND | 93% | QUARTZ SAND BURNING LOSS (1025°C) - 0.17% |
SiO2 | 99.7% | MgO | 0.003% |
POLYESTER RESIN | 6% | Al2O3 | 0.074% | K2O | 0.013% | |
TITANIUM OXIDE & OTHERS | 0.9% | Fe2O3 | 0.0042% | Na2O | 0.005% | |
CURING & COUPLING AGENT | 0.1% | CaO | 0.008% | TiO2 | 0.001% |
ADVANTAGES OF BESTONE'S ARTIFCIAL QUARTZ STONE |
S.N. | TEST ITEM | BESTONE QUARTZ STONE | MARBLE | GRANITE | CERAMIC TILE |
1 | RUPTURE STRENGTH | 45.8Mpa | ≧7.0Mpa | ≧8.0Mpa | ≧35.0Mpa |
2 | COMPRESSION STRENGTH | 222.0Mpa | ≧50.0Mpa | ≧100.0Mpa | ≧100.0Mpa |
3 | WATER ABSORPTION | 0.04% | ≦0.5% | ≦0.6% | ≦0.6% |
4 | MOHS' HARDNESS | 7 | 4-5 | 6-7 | 5-6 |
5 | ABRADABILITY | ≦70MM3 | ≧10MM3 | ≦150MM3 | ≦150MM3 |
ATTRIBUTES OF BESTONE'S ARTIFICIAL QUARTZ STONE |
HIGH HARDNESS |
COLOR TONE CONSISTENCY |
HIGH FLATNESS |
LOW WATER ABSORPTION |
HEAT RESISTANCE |
STAIN RESISTANCE |
SCRATCH RESISTANCE |
ACID&ALKALI RESISTANCE |
HIGH COMPRESS STRENGTH |
HIGH FLEXURAL STRENGTH |
➡ High Hardness and Low Water Absorption for Longevity ⬅ |
➡ Consistent Color Tone and High Flatness for a Seamless Look ⬅ |
➡ Heat, Stain, Scratch, Acid, and Alkali Resistance for Lasting Beauty ⬅ |
➡ Superior Compress and Flexural Strength for Robust Performance ⬅ |
PRODUCTION PROCESS OF ARTIFICIAL QUARTZ STONE SLAB |
BESTONE FACTORY |
RAW MATERIALS |
MIXING & CURING |
GRIND & CALIBRATE |
SURFACE POLISHING |
SLAB STOCKING |
Feeding & Mixing | Purified quartz granules and powder are poured into the mixing machine, together with unsaturated resin, pigments and antibiotic substance. |
Molding & Pressing | After mixing and blending, the mixture is poured into molds of 3050*1450mm (120'*57') or 3250*1650mm (128'*65'). Under vacuum and vibrating condition with high temperature and high pressure in a kiln, the mixture is finally formed into hard solid slabs. |
Grinding & Polishing | Slabs are moved to the Calibrating Machine to grind in required thickness. Then follow to be water polished. |
Edge Cutting | Rugged edges are clean-cut by Bridge Cutting Machine. |
QC & Packing | Finished slabs are strictly controlled in quality and classified. Only Grade A is used to export with wood-frame |
THE CAPACITY OF BESTONE'S FABRICATION CENTER |
CERTIFICATES, TESTING REPORTS & REWARDS |
RETAIL, WHOLESALE & PROJECT COORPERATION PARTNERS |
YOU MAY ALSO LIKE |
Calacatta Pristine | Calacatta Statuario | Calacatta Divine |
BACK TO TOP |